Application
Solvent-free adhesive suitable for all materials, ideal for durable bonding and repairs Specialty for cladding, stone fixing, Marble Jointings & All kind of civil works. The mixed mass is applied by brush or spatula on the surface to be adhered. The mix must be used within its pot-life. Curing normally takes place at room temperature within about 24 hours depending on the ambient temperature but may be accelerated by the application of heat. Bonds metal, wood, masonry, ceramics, glass, dry concrete, chipboard, leather, cardboard, fabric, rubber and most plastics (except polyethylene, polypropylene, PTFE)

Product Description

Lapox Ultra

Features

Lapox Ultra resin is a modified epoxy resin with thixotropic additives.
Lapox Ultra hardener is suitable to cure Ultra resin at ambient temperature.
The bonds prepared by system are suitable to achieve strong adhesion with similar and dissimilar substrates like glass to glass and glass to metal joining.

Applications:

Solvent-free adhesive suitable for all materials, ideal for durable bonding and repairs.
Specialty for cladding, stone fixing, Marble Jointings & All kind of civil works.
The mixed mass is applied by brush or spatula on the surface to be adhered. The mix must be used within its pot-life.
Curing normally takes place at room temperature within about 24 hours depending on the ambient temperature but may be accelerated by the application of heat.
Bonds metal, wood, masonry, ceramics, glass, dry concrete, chipboard, leather, cardboard, fabric, rubber and most plastics (except polyethylene, polypropylene, PTFE).

Advantages

High shear and peel strength, good electrical insulation properties, long working time, water resistance.

Technical Specifications

Pot life of 100 gm mix mass at 25 deg.
Resin & hardener were pre conditioned at 25 deg prior to checking pot life.
Properties after full cure.

Properties:

Value	Unit	Reference
Surface Dry of 8 mil Film @ 25 Degrres Centigrade 5895 180 200	minutes	ASTM D
Touch Dry of 8 mil Film @ 25 Degrres Centigrade 5895 460 480	minutes	ASTM D
Hard Dry of 8 mil Film @ 25 Degrres Centigrade 5895 760 780	minutes	ASTM D
Tensile Shear Strength Al-Al joint 1002 120 140	Kg/Sq. cm	ASTM D
After 24 hours @ 25 Degrres Centigrade

Processing Surface Preparation:

The adherents must be thoroughly degreased with a good degreasing solvent (e.g. toluene, acetone trichloroethlylene) and abraded with coarse emery paper or chemically etched. Inadequately pre-treated substrates may not bond satisfactorily.

Packing:

Retail: - 13gm, 36gm, 90gm, 180gm, 450gm, 900gm.

Bulk Pac for Projects : - 1.8Kg, 9Kg.

Tag: Lapox Epoxy Putty, Lapoquick Cynoacrylate Adhesives, Lapox Ultra, Marble Adhesive, La Seal water leak Sealant, Instant Adhesive, Transperant Adhesive

Trade Information

Payment Terms
Paypal, Cheque, Cash Advance (CA)
Main Export Market(s)
Africa, Middle East, Western Europe, Eastern Europe, South America, North America, Central America, Australia, Asia